General Characteristics: Thermoplastics Grades

CHARACTERISTICS CONDITIONS STANDARD UNITS RDG 314 RDG 277 7233 7033 6333 5533 MX 1940 4033 MX 1205 3533 2533

SHORE

HARDNESS

instantaneous ISO 868/ ASTM D 2240 Shore D 75 71 69 69 64 54 55 42 46 33 27
Shore A - - - - - - - 90 92 82 77
after 15 seconds ISO 868/ ASTM D 2240 Shore D 71 68 61 61 58 50 48 35 41 25 22
Shore A - - - - - - - 89 90 80 74
DENSITY   ISO 1183 g/cm3 1.12 1.12 1.01 1.01 1.01 1.01 1.01 1.00 1.01 1.00 1.00

MELTING

POINT

  ISO 11357/ ASTM D 3418 °C 175 174 174 172 169 159 154 160 147 143.5 133.5

VICAT SOFTENING

POINT

under 10 N ISO 306/ ASTM D 1525 °C 173 170 164 164 157 142 127 131 111 77 58

WATER ABSORPTION

AT EQUILIBRIUM

at 23°C and 50% RH ISO 62/ ASTM D 570 % 0.6 0.6 0.7 0.7 0.7 0.6 0.7 0.5 0.4 0.4 0.4

WATER ABSORPTION

SATURATION

24h in water at 23°C ISO 62/ ASTM D 570 % 0.9 1.0 0.9 0.9 1.1 1.2 1.7 1.2 1.2 1.2 1.2
MELT INDEX 235°C / 1kg ISO 1133/ ASTM D 1238 g/10 mn - - 4 6 5 7 - 5 9 8 10

LINEAR COEFFICIENT

OF THERMAL EXPANSION

from - 40°C to +140°C ASTM D 696 10-5/°C - - 12 16 14 17 - 19.5 20 21 20

SURFACE

RESISTIVITY

  IEC 60093/ ASTM D 257 Ohm/sq -
-
-
-
›1012

VOLUMIC

RESISTIVITY

  Ohm.cm
FILLER       Glass fiber - - - - - - - - -

Properties (Rubber Materials Tests)

CHARACTERISTICS CONDITIONS STANDARD EQUIVALENT UNITS 7233 7033 6333 5533 4033 MX 1205 3533 2533
TENSILE STRESS            to obtain extension of 10% v = 500 mm/min   ASTM D 638 MPa 28.7 21.6 14.2 10 5.1 5.5 1.6 1.1
50% 25 21.8 16.6 13.2 8.9 9.1 4.6 3.2
100% 24.8 21.1 16.9 13.6 10.5 9.1 5.8 4.2
TENSION SET                                               under 5% v = 500 mm/min ISO 2285 ASTM D 412
(method A)
% 0.8 0.5 0.5 0.5 0.4 0.5 0.4 0.4
  10%    
15%
2.4 1.9 1.5 1.5 1.2 1.2 0.7 0.5
4.2 3.8 3.3 2.9 2.1 2.3 0.9 0.8
20% 6.6 5.8 5.1 4.6 3.1 3.3 1.4 0.9
TEAR RESISTANCE unnotched ISO 34-1 ASTM D 624 kN/m 194 177 147 135 116 115 78 66
notched 166 149 127 106 85 77 50 44
TABER ABRASION RESISTANCE H18 / load 1kg / 1000 rotations ISO 9352   mm 54 59 60 62 62 60 77 99
ABRASION RESISTANCE 10 N / 40 m ISO 4649 DIN 53516 mm3 - - 55 47 48 40 64 130
RESILIENCE   ISO 4662 DIN 53512   - - 53 57 66 58 69 70
COMPRESSION SET        under deformation of      25% 70h at 23°C ISO 815   % - - 47 43 32 37 22 19
COMPRESSION SET                     under load of   9.3MPa 22h at 70°C   ASTM D 395
(method A)
% - - 5 10 21 - 54 62
RESISTANCE TO CRACKING BY REPEATED FLEXURE 20 °C – 100 000 flex ISO 133   mm - - 5 3 2 - 2 2
-20 °C – 50 000 flex - - 14 9 4.5 - 2.5 2.5

Properties (Plastic Materials Tests)

CHARACTERISTICS CONDITIONS STANDARD UNITS RDG 314 RDG 277 7233 7033 6333 5533 MX 1940 4033 MX 1205 3533 2533
FLEXURAL MODULUS   ISO 178 MPa 2200 1500 513 390 285 170 167 77 86 21 12
ASTM D 790 MPa - - 518 379 278 164 - 81 93 20 14
TENSILE MODULUS   ISO 527 MPa - - 522 384 280 161 - 71 81 18 10
ASTM D 638 MPa 2600 2000 521 383 287 160 158 74 79 20 10
TENSILE – STRESS AT YIELD v = 50 mm/min ASTM D 638 type IV MPa 62 50 26 22 18 12 12 - - - -
TENSILE – STRAIN AT YIELD % 6 10 18 20 22 25 25 - - - -
TENSILE – STRESS AT BREAK MPa 56 45 56 54 53 52 51 40 42 39 32
TENSILE – STRAIN AT BREAK % 10 17 ›300 ›350 ›350 ›450 ›550 ›450 ›550 ›600 ›750
IMPACT STRENGTH * (IZOD) AT + 23 °C unnotched ASTM D 256 J/m - - 1380 p 969 p 607 p N - N N N N
notched - - 192 c 847 p 554 p N - N N N N
IMPACT STRENGTH * (IZOD) AT - 40 °C unnotched
                                       
notched
ASTM D 256 J/m - - 2460 p 2345 p 1589 p 1589 p - N N N N
- - 50 c 50 c 11 c 1038 p - N N N N
IMPACT STRENGTH * (CHARPY) AT + 23 °C unnotched ISO 179 kJ/m2 - - N N N N N N N N N
notched - - 15 c 120 p N N N N N N N
IMPACT STRENGTH * (CHARPY) AT - 30 °C unnotched ISO 179 kJ/m2 - - N N N N N N N N N
notched 7.3 7.3 10 c 10 c 20 c N N N N N N

General Characteristics - Special Grades

  ANTISTATIC  
CHARACTERISTICS CONDITIONS STANDARD EQUIVALENT UNITS MH 1657 MV 1074 MV 1041 MP 1878 MV 3000 MV 6100 INIT 1100
SHORE HARDNESS instantaneous ISO 868 ASTM D 2240 Shore D 40 40 60 58 35 58 75
DENSITY   ISO 1183   g/cm3 1.14 1.07 1.04 1.09 1.02 1.04 1.12
MELTING POINT   ISO 11357 ASTM D 3418 °C 204 158 170 195 158 170 198
VICAT SOFTENING POINT under 10 N ISO 306 ASTM D 1525 °C 160 - - 169 - - -
FLEXURAL MODULUS at 23°C and 50% RH ISO 178 ASTM D 790 MPa 80 80 270 180 45 210 440
TENSILE – STRESS AT BREAK v = 50 mm/min ISO 527   MPa 32 30 44 60 35 48 71
TENSILE – STRAIN AT BREAK v = 50 mm/min ISO 527   % ›500 ›700 450 550 500 - ›300
WATER ABSORPTION AT EQUILIBRIUM at 23°C and 50% RH ISO 62 ASTM D 570 % 4.5 1.4 0.9 1.35 1 0.9 -
WATER ABSORPTION SATURATION 24h in water at 23°C ISO 62 ASTM D 570 % 120 48 12 6.7 28 11 -
MELT INDEX 235°C / 1kg ISO 1133 ASTM D 1238 g/10 mn 27 14 7 8     1.7
SURFACE RESISTIVITY   IEC 60093 ASTM D 257 Ohm/sq 1 10 9 3 10 9 - - - - -
VOLUMIC RESISTIVITY   Ohm.cm 2 10 9 2.5 10 9 - - - - -